Current position: Home > Products > Stainless Steel Strip > 316Stainless Steel Strip

Description of Product

316 stainless steel because of the addition of Mo element, so that its corrosion resistance, and high temperature strength has been greatly improved, high temperature resistance can reach 1200-1300 degrees, can be used under harsh conditions.
Application: Seawater equipment, chemical, dye, paper making, oxalic acid, fertilizer and other production equipment;
Photographs, food industry, coastal facilities, ropes, CD rods, bolts, nuts.

Equivalent Material of 316 Stainless Steel  Sheet

GradeEuronormChina GBJapanese JIS
No.
3161.44010Cr17Ni12Mo2SUS316

Product Parameter

Name

316 Stainless steel strip

Grade

201, 304, 316, 316L, 410, 430, etc

Standard

JIS, AISI, ASTM, DIN, TUV,BV,SUS,etc

Thickness

0.1–30mm

Width

range

1m,1.22m,1.25m,1.5m,etc

Length

Standard:2000/2438/3048mm

Size

1000mm*2000mm, 1219mm*2438mm, 1219mm*3048mm, or as required

Color

Golden, Black , Sapphire Blue, Brown, Rose gold, Bronze, Purple, gray, silver, Champagne, violet, blue diamond, etc

Surface 

2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc

Application

Interior/exterior/architectural/bathroom decoration, elevator decoration, hotel decoration, kitchen equipment, ceiling, cabinet, kitchen sink, advertising nameplate

Lead time

7 to 15 working days after the receipt of 30% deposit

Payment terms

TT ect.

Packing

Wooden pallet or according to customer’s request


Chemical Composition and Mechanical Properties of Stainless Steel Strips

Grade

Chemical Composition (%)

Mechanieal Performece

C

Si

Mn

P

S

Ni

Cr

Mo

Hardness

201

≤0.15

≤1.00

5.5/7.5

≤0.060

≤0.030

3.5/5.5

16.0/18.0

-

HB≤241,HRB≤100, HV≤240

304

≤0.08

≤1.00

≤2.00

≤0.045

≤0.03

8.0/11.0

18.00/20.00

-

HB≤187,HRB≤90,HV≤200

316

≤0.08

≤1.00

≤2.00

≤0.045

≤0.03

10.00/14.00

16.0/18.0

2.00/3.00

HB≤187, HRB≤90 HV≤200

316L

≤0.03

≤1.00

≤2.00

≤0.045

≤0.03

10.00/14.00

16.0/18.0

2.00/3.00

HB≤187, HRB≤90 HV≤200

410

≤0.15

≤1.00

≤1.25

≤0.060

≤0.030

≤0.060

11.5/13.5

-

HB≤183, HRB≤88 HV≤200

430

≤0.12

≤1.00

≤1.25

≤0.040

≤0.03

-

16.00/18.00

-

HB≤183, HRB≤88 HV≤200


The tensile strength (MPa) was 620 MIN
The yield strength (MPa) was 310 MIN
Elongation rate (%) 30 MIN
Area reduction (%) 40 MIN