Current position: Home > Products > Stainless Steel Coil > 316 316L Stainless Steel Coil

Description of Product

316 stainless steel because of the addition of Mo element, so that its corrosion resistance, and high temperature strength has been greatly improved, high temperature resistance can reach 1200-1300 degrees, can be used under harsh conditions. Application: Seawater equipment, chemical, dye, paper making, oxalic acid, fertilizer and other production equipment; Photographs, food industry, coastal facilities, ropes, CD rods, bolts, nuts


316L is a stainless steel material grade, AISI 316L is the corresponding American grade, SUS 316L is the corresponding Japanese grade.
China's uniform digital code for S31603, the standard grade for 022CR17NI12MO2 (new standard), the old grade for 00CR17NI14MO2, said it mainly contains Cr, Ni, Mo, the number says it probably contains a percentage.

Equivalent Material of 316 316L Stainless Steel  Coil

GradeEuronormChina GBJapanese JIS
No.
3161.44010Cr17Ni12Mo2SUS316
316L1.4404022Cr17Ni12Mo2SUS316L

Standard Specification Of 316 316L Coil

Name316 316L Stainless Steel Coil
Thickness4mm-100mm
Width1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Surface2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc
FinishHot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats,
Blank (Circle), Ring (Flange) etc.

316 stainless steel composition content

GradeCMnSiPSCrMoNiN
316Min.
Max.
≤0.08≤2.00≤1.00≤0.035≤0.0316.0-18.52.0-3.010.0-14.0-
316L≤0.03≤2.00≤1.00≤0.045≤0.0316.0-18.02.0-3.010.0-14.0-
316316L
The tensile strength (MPa) was 620 MIN
The yield strength (MPa) was 310 MIN
Elongation rate (%) 30 MIN
Area reduction (%) 40 MIN
Tensile strength σb (MPa) : ≥480
Conditional yield strength σ0.2 (MPa) : ≥177
Elongation Δ5 (%) : ≥40
Section shrinkage ψ(%) : ≥60
Hardness: 187 hb or less;
90 HRB or less;
200 hv or less
Density: 7.98g/cm3;
Specific heat capacity ratio (20℃) : 0.502J/(g*K)